SK95 Zirconia ceramic balls
Composition
94.8%ZrO2,5.2%Y2O3
Kg/L
7mm)
g/cm3
Hardness(HV)
1250
Gpa
Thermal Conductivity
3
KN
7mm)
Mpa.m1-2
Grain size
0.5
)
(20-4009.6
Yttium stabilized zirconia ceramic grinding beads
spherical shape tolerance and surface roughness
Vdws
Ra
3
0.08
5
0.13
10
0.25
16
0.4
20
0.5
24
0.6
28
0.7
40
1
60
1.5
100
2.5
200
5
min=Dmin=Wg*3;
(2). The initial and desired particle size of product:
Dmin D1*30 50;
(3). The diameter with 1.5m is a good started point.
4.How to calculate the Yttria stabilized zirconia beads?
Type of mills
Closed
Open(Vertical)
Basket mills
Mixer
Horizontal
Vertical
Rate(V%)
75-85
70-80
60-70
60-80
20-60
5.How to keep the beads away from breakage and wear?
(1). The beads charge is not over the maximum limit (suggested 85%).
(2). Different beads adapt to limited tip speeds.
(3).Select different material beads depend on mill base viscosity.
(4).Do not mix different brands of beads.
(5).Try to use the narrow tolerance size beads.
(6). Washing the milling chamber with beads at low speed(suggested below 100rpm).
(7). A periodic sieving the beads away under the minimum limitation.
(8). A periodic inspection of the separator and cover wearing plate enables the users to fine the worn parts.
Our company can
produce Zirconia fine ceramic liners of ball mills according to customers'
demand,such as Zirconia fine ceramic tiles,Zirconium ceramic chips,Zirconia
fine ceramic shaft sleeves,Zir
High-grade Zirconium Silicate powder is a kind of superfine material manufactured under strict process and quality control of laboratory conditions,it is recommended for high-quality enamel ware.
Fused Zirconia powder is produced using azorite as raw
material,going though the process of electro-cast,desilication,and followed by
a series of refining process.It is the main material for Zirconi
Fused Zirconia powder is produced using azorite as raw
material,going though the process of electro-cast,desilication,and followed by
a series of refining process.It is the main material for Zirconi