Осажденный Silica (порошок)
|
|
1. Content of SiO2: min. 96.0%2. White powder3. pH value: 6.54. Loss on heating: 6.30%5. Ignition loss (dry basis): 4.1%6. DBP absorbing value: 2.52cm3/g7. As a re-forcing filler in shoe industry, it
|
|
|
|
Осажденный Silica Granular
|
|
ZQ-356K(GRANULAR)Specific surface CTAB m2/g 186Content of silica%(dry basis) 97.5Heating decrement% 6.2Ignition decrement% 4.3Iron content mg/kg 350DBP absorption cm3/g 2.50PH value 6.945um residue %
|
|
|
|
Осажденный Silica Zq356
|
|
|
ZQ-356(POWDER)Specific surface CTAB m2/g 184Content of silica%(dry basis) 97.3Heating decrement% 6.3Ignition decrement% 4.3Iron content mg/kg 330DBP absorption cm3/g 2.51PH value 6.845um residue % 0.0
|
|
|
|
Осажденный Silica Zq356
|
|
ITEM ZQ-356K(GRANULAR)Specific surface CTAB m2/g 186Content of silica%(dry basis) 97.5Heating decrement% 6.2Ignition decrement% 4.3Iron content mg/kg 350DBP absorption cm3/g 2.50PH value 6.945um resid
|
|
|
|
|
|
Кварцевый
|
|
|
ITEM ZQ-356K(GRANULAR)Specific surface CTAB m2/g 186Content of silica%(dry basis) 97.5Heating decrement 6.2Ignition decrement% 4.3Iron content mg/kg 350DBP absorption cm3/g 2.50PH value 6.945um residu
|
|
|
|
Гранулят Silica
|
|
|
Spec.SurfaceArea(N2) M2/g 175Heating Loss 6.5PH-Value 6.2Density g/l 305SiO2-Content 98Appearance White granules
|
|
|
|
Осажденный Silica
|
|
|
ITEM ZQ-356(POWDER) ZQ-356K(GRANULAR)Specific surface CTAB m2/g 184 186Content of silica%(dry basis) 97.3 97.5Heating decrement% 6.3 6.2Ignition decrement% 4.3 4.3Iron content mg/kg 330 350DBP absorpt
|
|
|
|
Гранулят Осажденный Silica
|
|
|
1. Content of SiO2: min. 96.0%2. Granular3. pH value: 6.54. Loss on heating: 6.30%5. Ignition loss (dry basis): 4.1%6. DBP absorbing value: 2.52cm3/g7. As a re-forcing filler in shoe industry, it has
|
|