#233 Working time:70min./100g Soft-viscous/25 Curing time:40min.(90 ) / 12hrs(R.T.) Excellent electrical characteristics.UL approved. For assembling/fixing/bonding/coating of electronic parts.

#901S Working time:60~80min. 6000cps/25 Curing time:4hrs. Standard type. Low viscosity. No toxicity. High pressure-resistance. For general bonding, civil engineering, architecture and filling.

901SC Working time:70min./100g Semi-paste/25 Curing time:4hrs. No toxicity. Low fluidity. Flexible for operation. Excellent weathering and chemical-resistance after full cure. For general bonding, c

#902 Working time:60~90min./100g Paste/25 Curing time:4hr. Stabdard/non-sag.Tough. Same as #901.Also suitable for vertical,overhead surface or porous materials.

#911 Working time:4min./100g 10000cps/25 Curing time:15min.. Fast cure type.Cure in 15 min.even with small amount like 1g. For quick bonding of most materials,electronic parts and urgent repair.

#911-2 Working time:3min./100g 10000cps/25 Curing time:10min.. Super fast cure,water base,really clear.tough,high impact-resistant,bonding strength over 250kg/cm2. For quick bonding of most material

#911S Working time:12min./100g 8000cps/25 Curing time:40min.. General type.Strong bonding strength.Tough.Easy to use. Mid-cure for bonding of family handicraft.

#912 Working time:6min./100g Paste/25 Curing time:20min.. Fast cure/non-sag type. Same as #911.Also suitable for vertical,overhead surfaces or porous materials.

#941 Working time:200min./100g 5000cps/25 Curing time:24hrs.. Low reaction temp.(42 ).Cure on low-temp. and wet surfaces or in water.Excellent resistance to organic acid. For low-temp,large area or