silicone sealant with special appearance
NOTE After operating, the rest of glue must be sealed to store , and tightened the cap immediately. when using it in the next time, if there is a little crust in sealed place, to remove it and it will not affect the normal application. the process of storage , the canal orifices may appear the phenomenon of the curing, to clean it then it can be used again, and the performance of product is not affected.Before The Curing AppearanceWhite PasteTack Free Time≤10 (min)Extrudability 5~11 (g/s,25℃)Cure Time 3~7(d)After the curing Relative Density1.40~1.45 (g/cm3)Tensile Strength≥2.5 (MPa)Break Elongation≥500 (%) Shear Strength≥2.0 (MPa)Hardness 45~55 (Shore A)The Temperature Range-60~200 (℃)Volume Resistivity2.6×1015 (Ω·CM)Dielectric Strength20 (kV/·mm)Dielectric Constant3.12Flame Retardant Grade UL94 HB Sample: 300mL / tube, 25tubes / box.
Before The Curing AppearanceWhite PasteTack Free Time≤10 (min)Extrudability 5~11 (g/s,25℃)Cure Time 3~7(d)After the curing Relative Density1.40~1.45 (g/cm3)Tensile Stren
1. Features ZS-NJ-D939C is one kind of the one-component dealcoholized silicone sealant at room temperature curing with medium viscosity. This product has the properti
1. Features ZS-NJ-D939C is one kind of the one-component dealcoholized silicone sealant at room temperature curing with medium viscosity. This product has the properti
Before the curingAppearanceWhite pasteRelative density1.60~1.70(g/cm3)Surface drying time≤15(min)After the curingTensile strength≥1.5(MPa) Elongation At Break≥150(%)Shear strength&
INSTRUCTIONS1、Clean surface: cleaning adhesion surface and to remove the rust,dust and greasy dirt, etc.2、After sizing: Unscrew the hose cap (or cutting), squeezing the glue on cleaned surface, so
METHOD OF OPERATIONINSTRUCTIONS1、Clean surface: cleaning adhesion surface and to remove the rust,dust and greasy dirt, etc.2、After sizing: Unscrew the hose cap (or cutting), squeezing the glue on
Before The Curing Appearance Semi Transparent And Semi FlowSpecific Gravity0.95~1.05 (g/cm3)Surface Drying Time ≤15 (min)Curing Time 3~7 daysAfter The CuringTensi
Before The Curing Appearance Semi Transparent And Semi FlowSpecific Gravity0.95~1.05 (g/cm3)Surface Drying Time ≤15 (min)Curing Time 3~7 daysAfter The CuringTensi