D3/1.2080 tool steel flat bar
|
|
1.2080/Cr12/D3/Cr8/Cr10 cold work tool steel flat bar
1. Chemical composition:
C 2.0~2.3
Si≤0.40
Mn≤0.40
Cr11.50~13.00
P≤0.030
S≤0.030
2. Delivery condition:
Hot rolled o
|
| |
|
D5/Cr12MoV tool steel forged steel bar
|
|
1) Delivery condition : hot rooled or forging. EAF or ESR material ;
2) Surface : black or machined surface .
3) Annealing hardness : HBS=207-255;
4)Compared steel : D5(USA AISI) , Cr12
|
| |
|
DIN1.2738 Mould steel
|
|
DIN1.2738 Mould steel
DIN1.2738has good mechanical property and quenching ,, after deal with it , it will be made the surface have equal surface ,.
DIN1.2738 has nice polishing
|
|
|
|
H11/1.2343 hot work alloy tool steel
|
|
1.2343/H11 ALLOY TOOL STEEL
1. Grade:
AISI:H11/ASTM:H11/JIS:SKD6/DIN:1.2343/GB: 4Cr5MoSiV
2. Specification:
Diameter/Thickness: 20~600mm
or as customers’ requires
|
| |
|
H13/1.2344 hot work tool steel
|
|
H13/1.2344/SKD61 HOT WORK TOOL STEELSpecificationsChemical Composition ELEMENTMIN.MAX.CARBON0.370.42MANGANESE0.200.50PHOSPHORUS00.025SULFUR00.005SILICON0.801.20CHROMIUM5.005.50VANADIUM0.801.20MOLYBDEN
|
| |
|
H21 Hot work steel
|
|
H21 Hot work steel
1)Delivery condition :Hot rolled or forging ,ESRor EAF material ,black or machined surface
2)Comparable steel : 3Cr2W8V (GB), H21 (AISI) ,1.2581 (DIN ), SKD5(JIS )
|
|
|
|
NAK80 steel round bar
|
|
Forged Steel NAK80
1Ni3Mn2CuAlMo / NAK80 is low allloy separate out induration steel . it has good machanical property after the heat-treatment .
1Ni3Mn2CuAlMo / NAK80 is high quenchi
|
| |
|
O1/1.2510 oil tool steel
|
|
AISI O1(DIN 1.2510, GB 9CrWMn,JIS SKS3) OIL TOOL STEEL 1. Chemical composition: C=0.85~0.95, Si=0.20~0.40, Mn=1.00~1.30, Cr=0.40~0.60, W=0.40~0.60, V=0.10~0.20.2. Delivery condition: EAF or ESR,
|
| |
|
P20+Ni Mould steel
|
|
1. Grade: P20+Ni/718/1.2738 steel block
2. Specification: T200~800*W400~1000*L1500~5800mm
3. Delivery condition: Forging, machined surface
4. Chemical composition(for refere
|
|